Description of products
This product is made of polyethylene resin as the main raw material, adding carbon black, lubricant and other additives, by mixing, plasticizing and granulating. This material has excellent dielectric properties, resistance to low temperature and environmental stress cracking properties. It is suitable for the outer protective layer of communication optical cable, signal cable and control cable.
Product category
Product name
|
Model
|
Low density polyethylene sheathing for optical cable
|
KJPE-LD7008
|
Middle Density polyethylene sheathing for optical cable
|
KJPE-MH7108
|
High Density polyethylene sheathing for optical cable
|
KJPE-GH8008
|
Technical indicators
Item |
KJPE-LD7008
|
KJPE-MH7108
|
KJPE-GH8008
|
Densityg/cm3
|
<0.940
|
0.940-0.955
|
0.955-0.978
|
bow wrinkle resistance ≥N/cm3
|
14.0
|
19.0
|
20.0
|
fracture growth rate ≥%
|
600
|
600
|
650
|
low temperature impact embrittlement temperature-76°C
|
IMS
|
passing
|
|
2(TC時(shí)volume resistivityΩ.m≥
|
1*1014
|
1*1014
|
1*1014
|
dielectric strength≥MV/m
|
25
|
25
|
25
|
dielectric constant
|
<2.80
|
<2.75
|
<2.75
|
dielectric loss factor
|
/
|
<0.005
|
<0.005
|
after ageing
|
test temperature°C
|
100±2
|
110±2
|
110±2
|
time h
|
240
|
240
|
240
|
|
|
tensile strength≥
|
13.0
|
16.0
|
20.0
|
|
tensile strain at break ≥
|
500
|
500
|
650
|
carbon black content%
|
2.60±0.25
|
2.60±0.25
|
2.60±0.25
|
dispersion grade of carbon black≤
|
3
|
3
|
3
|
200。(: oxidation induction time(OIT) min≥
|
40
|
40
|
40
|
solution flow rate g/10min≤
|
2.0
|
1.5
|
1.0
|
vicat softening point°C≥
|
/
|
110
|
110
|
resistance to environmental stress crackingFo/h≥
|
500
|
500
|
500
|
Storage and packaging
Fiber optic cable with polyethylene sheathed material inside the bag with polyethylene film bag, outer bag with woven bag. The company generally uses 750kg/ bag large packaging, but also according to the need to use 25kg/ bag packaging or other forms of packaging. This product should be stored in a clean, cool, dry, ventilated warehouse.
|