Description of products
KJFZ - UV is a kind of applied in solar photovoltaic cable insulation or sheath on the radiation crosslinking of low smoke zero halogen flame retardant cable materials, the highest use level, such as the temperature of 125 ° CO products have excellent mechanical and physical properties, electric properties, processing performance, flame retardant performance, as well as excellent resistance to high temperature aging resistance can, in the production of cable has a longer service life.
Main performance indicators
Item
|
Unit
|
Technical requirements
|
KJFZ-UV
|
Density
|
g/cm3
|
£1.50
|
tensile strength
|
Mpa
|
>10.0
|
elongation at break
|
%
|
>200
|
thermal ageing 150°CX168h
|
tensile strength retention rate
|
%
|
>70
|
elongation at break retention rate
|
%
|
>70
|
thermal extension 200°C *0.2MPa*15min
|
eElongation under load
|
%
|
《70
|
permanent deformation after cooling
|
<20
|
dielectric strength
|
MV/m
|
>20
|
2CTCvolume resistivity
|
Q?m
|
>1x1012
|
low temperature impact embrittlement temperature
|
°C
|
-30
|
oxygen index
|
%
|
>30
|
halogen acid gas content
|
mg/g
|
<5
|
pH value
|
/
|
24.3
|
Electrical conductivity
|
Us/mm
|
<10
|
resistance to hot and humid 90°C*1000h
|
tensile strength gradient
|
%
|
±30
|
elongation at break gradient
|
±30
|
smoke density
|
flameless
|
Ds max
|
<350
|
with flame
|
<150
|
thermal impact test 150°Cx1h
|
/
|
no cracking
|
thermal life test 180°C*100h
|
elongation at break retention rate
|
%
|
250
|
acid and alkali resistant (23°C*168h)
|
tensile strength retention rate
|
%
|
>70
|
elongation at break retention rate
|
280
|
Processing technology
This product processing uses low smoke halogen free special screw. The length diameter ratio of extruding screw is 18~25, the compression ratio is 3:1, the temperature control of each area of the barrel should have a cooling device.
Model
|
barrel temperature
|
head temperature
|
KJFZ-UV
|
130-150°C
|
150-165°C
|
Notes
① Before processing, ensure that screw, barrel and hopper are thoroughly cleaned, and impurities are strictly prohibited in the 3 processes of processing.
② Once the raw materials are opened, it is recommended to use them within 24 hours. If the package is damaged, it should be dried before use.
|