Description of products
KJPE-ZPE8028C . KJPE-ZPE8029B . KJPE-ZPE8030A是以中高Density聚乙烯樹脂為主要原料，加入適量 的阻燃劑、抗氧劑等多種加工助劑，經混合、塑化、擠出、造料而成，具有良好的抗開裂耐低溫性能，良好 的阻燃及加工性能，使用本材料生產的電纜可通過IEC60332規定的成束垂直燃燒試驗，適用于中低壓電力 電纜等。
Main performance indicators
|
Item
|
Unit
|
Technical requirements
|
|
KJPE-ZPE8028C
|
KJPE-ZPE8029B
|
KJPE-ZPE8030A
|
|
Density
|
g/cm3
|
W1.32
|
W1.32
|
W1.32
|
|
tensile strength
|
Mpa
|
212.5
|
>13
|
>14
|
|
elongation at break
|
%
|
2400
|
2400
|
2500
|
|
thermal ageing tensile strength gradient
|
%
|
±25
|
±25
|
±25
|
|
110°Cx240helongation at break gradient
|
%
|
±25
|
±25
|
±25
|
|
thermal deformation 70°Cx5h
|
%
|
<50
|
<50
|
<50
|
|
dielectric strength
|
MV/m
|
>18
|
>18
|
>18
|
|
20°Cvolume resistivity
|
Ω?m
|
21x10"
|
21x10"
|
21x10"
|
|
low temperature impact embrittlement temperature
|
°C
|
-40
|
-40
|
-40
|
|
oxygen index
|
%
|
>26
|
>28
|
>30
|
|
carbon black content(for black sheath only)
|
%
|
3.0±1.0
|
3.0±1.0
|
3.0±1.0
|
|
200°C oxidation induction time(OIT)
|
min
|
>30
|
>30
|
>30
|
|
resistance to environmental stress crackingFo/h
|
Fo/h
|
>500
|
>500
|
2500
|
|
thermal shock (130°Cx1h)
|
/
|
no cracking
|
no cracking
|
no cracking
|
Processing technology
This product processing performance is superior, suitable for extrusion pipe, half extrusion pipe, extrusion die extrusion. The length-diameter ratio of the extrusion screw is 18-25, the compression ratio is 3:1, and the temperature control in each area of the barrel should have a cooling device.
| Model |
Barrel temperature |
Nose temperature |
|
KJPE-ZPE8028C/KJPE-ZPE8029B/KJPE-ZPE8030A |
140~160°C |
150~170°C |
Notes
① Before processing, ensure that screw, barrel, hopper thoroughly clean, processing H process is strictly prohibited to bring impurities.
② Once the raw materials are opened, it is recommended to use them within 24 hours. If the package is damaged, it should be dried before use.
|